Hydroxyapatite (HA) nanopowders are attracting interest for surface application to ceramic biomaterials. In this study, we developed innovative and new viable synthesis routes of calcium phosphate nanopowders from the natural calcium carbonate of chicken eggshells. Following the four routes, alternative co-precipitation, vacuum process, brushite, and calcination, we obtained the HA samples, which were then characterized by different methods. The X-ray diffraction /Rietveld method showed the HA phases, monetite and brushite crystallinity with greater symmetry, and nanoscale. Transmission electron microscopy showed the morphology of nanoparticles functionalized nanoparticles smaller than 100 nm in routes A, B and D, and Fourier-transform infrared spectrophotometry and Raman spectroscopy identified the classic chemical groups of calcium phosphates by four routes mainly groups (PO4)3- and (CO3-). Scanning electron microscopy analysis revealed a good surface topography to future cell biointeraction in A, B and D routes, and thermogravimetric analysis showed the mass loss profile inherent to each synthesis route with slot at 200 °C. Hence, the eggshell HA and brushite and the specific monetite nanoparticles with different morphology can be prepared from the four new possible and viable routes using different methods.

The incorporation of zinc onto biomaterials may improve their biological properties, since it is an essential trace element, involved on important steps of bone remodeling. The aim of this work was to evaluate the in vivo biocompatibility of previously characterized hydroxyapatite granules incorporated with 5% zinc (ZnHA), through a subcutaneous grafting test. Granules produced from powders of ZnHA or stoichiometric HA were subcutaneously grafted onto Balb/c mice, and histomorphometrical analysis was performed at 7, 14, 21, 28 or 60 days after grafting. HA and ZnHA induced a similar foreign body reaction, with formation of granulome and the presence of a fibrous capsule. Granulocytes were virtually absent, and agranulocytes decreased with time. ZnHA treated samples presented faster reduction on multinucleated giant cells and increase on observed angiogenesis, as compared to HA. It could be concluded that ZnHA granules are biocompatible. Further study should better address its potential use for bone therapy.

Hydroxyapatite (HA) is capable of accepting substitute ions within its lattice, including zinc ions. Zinc is a trace element that activates the osteogenesis of osteoblastic cells and therefore plays an important role in the activity of alkaline phosphatase enzyme. The purpose of this work was to produce and characterize 5% mol Zn bioceramic in granular form (Zn-granules) for clinical applications and compare it with granules made from HA by using the same production route. Granules with addition of porogen agents were produced from powders of HA and zinc-containing HA by uniaxial pressing and heat treatment. The granules were subsequently ground and sieved. The results indicated that zinc contributed to the reduction of sample crystallinity and formed a biphasic structure after calcination at 1200 °C. Additionally, zinc release from granular material may have clinical applications as bone graft.